塑胶原料 > 产品中心 > LCP美国杜邦6130

LCP美国杜邦6130 WT010

LCP美国杜邦6130 WT010

2023-06-30

LCP美国杜邦6130 WT010 产品规格:

Celanese Zenite® 6130 WT010 LCP

Material Notes:  Zenite® 6130 WT010 is a 30% glass reinforced white liquid crystal polymer resin with a heat deflection temperature of 268°C.
Celenese acquired the Zenite product line from DuPont in 2010.

Physical Properties Metric English Comments
Specific Gravity  1.67 g/cc 1.67 g/cc ASTM D 792
Density  1.68 g/cc 0.0607 lb/in³ ISO 1183
Filler Content  0.3 0.3 　
Moisture Absorption  0.00002 0.00002 50%RH,23°C,24h; ASTM D570
　 @Thickness 3.17 mm @Thickness 0.125 in 　
Water Absorption at Saturation  0.0008 0.0008 Water, tap 23°C,10000h; ASTM D570
　 @Thickness 3.20 mm @Thickness 0.126 in 　
Linear Mold Shrinkage, Flow   -0.000700 cm/cm -0.000700 in/in ASTM D955
　 @Thickness 0.787 mm @Thickness 0.0310 in 　
　 -0.000700 cm/cm -0.000700 in/in ASTM D955
　 @Thickness 15.7 mm @Thickness 0.620 in 　
　 -0.000700 cm/cm -0.000700 in/in ASTM D955
　 @Thickness 3.17 mm @Thickness 0.125 in 　
Linear Mold Shrinkage, Transverse   0.0050 cm/cm 0.0050 in/in ASTM D955
　 @Thickness 0.800 mm @Thickness 0.0315 in 　
　 0.0050 cm/cm 0.0050 in/in ASTM D955
　 @Thickness 3.17 mm @Thickness 0.125 in 　
　 0.0080 cm/cm 0.0080 in/in ASTM D955
　 @Thickness 1.60 mm @Thickness 0.0630 in 　
　 　 　 　
Mechanical Properties Metric English Comments
Hardness, Rockwell M  61 61 ASTM D 785
Hardness, Rockwell R  108 108 ASTM D 785
Tensile Strength at Break  130 MPa 18900 psi ISO 527
Tensile Strength, Ultimate   14.0 MPa 2030 psi ASTM D638
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 250 °C Temperature 482 °F 　
　 21.0 MPa 3050 psi ASTM D638
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 250 °C Temperature 482 °F 　
　 22.0 MPa 3190 psi ASTM D638
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 200 °C Temperature 392 °F 　
　 35.0 MPa 5080 psi ASTM D638
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 200 °C Temperature 392 °F 　
　 50.0 MPa 7250 psi ASTM D638
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 150 °C Temperature 302 °F 　
　 55.0 MPa 7980 psi ASTM D638
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 150 °C Temperature 302 °F 　
　 60.0 MPa 8700 psi ASTM D638
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 120 °C Temperature 248 °F 　
　 82.0 MPa 11900 psi ASTM D638
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 120 °C Temperature 248 °F 　
　 125 MPa 18100 psi ASTM D638
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 165 MPa 23900 psi ASTM D638
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 185 MPa 26800 psi ASTM D638
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature -40.0 °C Temperature -40.0 °F 　
　 250 MPa 36300 psi ASTM D638
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature -40.0 °C Temperature -40.0 °F 　
Elongation at Break  0.022 0.022 ISO 527
　 0.027 0.027 ASTM D 638
　 @Temperature 23.0 °C @Temperature 73.4 °F 　
Tensile Modulus  13.5 GPa 1960 ksi ISO 527
　 @Temperature 23.0 °C @Temperature 73.4 °F 　
　 3.40 GPa 493 ksi ASTM D638
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 250 °C Temperature 482 °F 　
　 4.00 GPa 580 ksi ASTM D638
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 250 °C Temperature 482 °F 　
　 4.80 GPa 696 ksi ASTM D638
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 200 °C Temperature 392 °F 　
　 6.70 GPa 972 ksi ASTM D638
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 150 °C Temperature 302 °F 　
　 8.30 GPa 1200 ksi ASTM D638
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 120 °C Temperature 248 °F 　
　 10.0 GPa 1450 ksi ASTM D638
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 200 °C Temperature 392 °F 　
　 12.0 GPa 1740 ksi ASTM D638
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 120 °C Temperature 248 °F 　
　 12.0 GPa 1740 ksi ASTM D638
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 150 °C Temperature 302 °F 　
　 14.0 GPa 2030 ksi ASTM D638
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 15.0 GPa 2180 ksi ASTM D638
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 20.0 GPa 2900 ksi ASTM D638
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature -40.0 °C Temperature -40.0 °F 　
　 29.0 GPa 4210 ksi ASTM D638
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature -40.0 °C Temperature -40.0 °F 　
Flexural Strength  190 MPa 27600 psi ISO 178
　 @Temperature 23.0 °C @Temperature 73.4 °F 　
　 17.0 MPa 2470 psi ASTM D790
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 250 °C Temperature 482 °F 　
　 22.0 MPa 3190 psi ASTM D790
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 250 °C Temperature 482 °F 　
　 23.0 MPa 3340 psi ASTM D790
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 250 °C Temperature 482 °F 　
　 33.0 MPa 4790 psi ASTM D790
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 200 °C Temperature 392 °F 　
　 45.0 MPa 6530 psi ASTM D790
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 200 °C Temperature 392 °F 　
　 50.0 MPa 7250 psi ASTM D790
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 200 °C Temperature 392 °F 　
　 50.0 MPa 7250 psi ASTM D790
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 150 °C Temperature 302 °F 　
　 62.0 MPa 8990 psi ASTM D790
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 120 °C Temperature 248 °F 　
　 64.0 MPa 9280 psi ASTM D790
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 150 °C Temperature 302 °F 　
　 70.0 MPa 10200 psi ASTM D790
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 150 °C Temperature 302 °F 　
　 80.0 MPa 11600 psi ASTM D790
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 120 °C Temperature 248 °F 　
　 90.0 MPa 13100 psi ASTM D790
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 120 °C Temperature 248 °F 　
　 170 MPa 24700 psi ASTM D790
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 195 MPa 28300 psi ASTM D790
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 195 MPa 28300 psi ASTM D790
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 245 MPa 35500 psi ASTM D790
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature -40.0 °C Temperature -40.0 °F 　
　 295 MPa 42800 psi ASTM D790
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature -40.0 °C Temperature -40.0 °F 　
　 340 MPa 49300 psi ASTM D790
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature -40.0 °C Temperature -40.0 °F 　
Flexural Modulus  11.0 GPa 1600 ksi ISO 178
　 @Temperature 23.0 °C @Temperature 73.4 °F 　
　 2.80 GPa 406 ksi ASTM D790
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 250 °C Temperature 482 °F 　
　 3.40 GPa 493 ksi ASTM D790
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 250 °C Temperature 482 °F 　
　 4.10 GPa 595 ksi ASTM D790
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 250 °C Temperature 482 °F 　
　 4.80 GPa 696 ksi ASTM D790
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 200 °C Temperature 392 °F 　
　 5.50 GPa 798 ksi ASTM D790
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 150 °C Temperature 302 °F 　
　 6.20 GPa 899 ksi ASTM D790
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 120 °C Temperature 248 °F 　
　 6.20 GPa 899 ksi ASTM D790
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 200 °C Temperature 392 °F 　
　 6.90 GPa 1000 ksi ASTM D790
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 200 °C Temperature 392 °F 　
　 6.90 GPa 1000 ksi ASTM D790
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 150 °C Temperature 302 °F 　
　 8.30 GPa 1200 ksi ASTM D790
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 120 °C Temperature 248 °F 　
　 9.00 GPa 1310 ksi ASTM D790
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 150 °C Temperature 302 °F 　
　 10.0 GPa 1450 ksi ASTM D790
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 120 °C Temperature 248 °F 　
　 12.0 GPa 1740 ksi ASTM D790
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 15.0 GPa 2180 ksi ASTM D790
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature -40.0 °C Temperature -40.0 °F 　
　 15.0 GPa 2180 ksi ASTM D790
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 19.0 GPa 2760 ksi ASTM D790
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 19.0 GPa 2760 ksi ASTM D790
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature -40.0 °C Temperature -40.0 °F 　
　 25.0 GPa 3630 ksi ASTM D790
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature -40.0 °C Temperature -40.0 °F 　
Compressive Strength  105 MPa 15200 psi ASTM D 695
Shear Strength   51.0 MPa 7400 psi ASTM D732
　 @Thickness 3.17 mm @Thickness 0.125 in 　
　 68.0 MPa 9860 psi ASTM D732
　 @Thickness 0.800 mm @Thickness 0.0315 in 　
Izod Impact, Notched   1.10 J/cm 2.06 ft-lb/in ASTM D256
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature -40.0 °C Temperature -40.0 °F 　
　 1.25 J/cm 2.34 ft-lb/in ASTM D256
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 2.00 J/cm 3.75 ft-lb/in ASTM D256
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 2.15 J/cm 4.03 ft-lb/in 40%NB; ASTM D256
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 3.00 J/cm 5.62 ft-lb/in ASTM D256
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature -40.0 °C Temperature -40.0 °F 　
Izod Impact, Unnotched   6.55 J/cm 12.3 ft-lb/in ASTM D4812
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 6.85 J/cm 12.8 ft-lb/in ASTM D4812
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 7.35 J/cm 13.8 ft-lb/in ASTM D4812
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature -40.0 °C Temperature -40.0 °F 　
　 440 J/cm 824 ft-lb/in ASTM D4812
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature -40.0 °C Temperature -40.0 °F 　
　 NB NB ASTM D4812
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
Izod Impact, Notched (ISO)   20.0 kJ/m² 9.52 ft-lb/in² ISO 180/1A
　 @Temperature -40.0 °C @Temperature -40.0 °F 　
　 25.0 kJ/m² 11.9 ft-lb/in² ISO 180/1A
　 @Temperature 23.0 °C @Temperature 73.4 °F 　
Izod Impact, Unnotched (ISO)   30.0 kJ/m² 14.3 ft-lb/in² ISO 180/1U
　 @Temperature -30.0 °C @Temperature -22.0 °F 　
　 35.0 kJ/m² 16.7 ft-lb/in² ISO 180/1U
　 @Temperature 23.0 °C @Temperature 73.4 °F 　
Charpy Impact Unnotched   2.50 J/cm² 11.9 ft-lb/in² ISO 179/1eU
　 @Temperature -30.0 °C @Temperature -22.0 °F 　
　 3.50 J/cm² 16.7 ft-lb/in² ISO 179/1eU
　 @Temperature 23.0 °C @Temperature 73.4 °F 　
Charpy Impact, Notched   2.50 J/cm² 11.9 ft-lb/in² ISO 179/1eA
　 @Temperature -30.0 °C @Temperature -22.0 °F 　
　 3.50 J/cm² 16.7 ft-lb/in² ISO 179/1eA
　 @Temperature 23.0 °C @Temperature 73.4 °F 　
　 　 　 　
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+17 ohm-cm 1.00e+17 ohm-cm ASTM D 257
Surface Resistance  1.00e+16 ohm 1.00e+16 ohm ASTM D 257
Dielectric Constant   3.6 3.6 0.8mm (0.031in); ASTM D 150
　 @Frequency 1.00e+6 Hz, @Frequency 1.00e+6 Hz, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 3.9 3.9 3.2mm (0.125in); ASTM D 150
　 @Frequency 1.00e+6 Hz, @Frequency 1.00e+6 Hz, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 4 4 0.8mm (0.031in); ASTM D 150
　 @Frequency 1000 Hz, @Frequency 1000 Hz, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 4.3 4.3 0.8mm (0.031in); ASTM D 150
　 @Frequency 1.00e+6 Hz, @Frequency 1.00e+6 Hz, 　
　 Temperature 120 °C Temperature 248 °F 　
　 4.3 4.3 1.6mm (0.062in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 4.3 4.3 3.2mm (0.125in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 4.4 4.4 0.8mm (0.031in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 150 °C Temperature 302 °F 　
　 4.4 4.4 1.6mm (0.062in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 150 °C Temperature 302 °F 　
　 4.4 4.4 3.2mm (0.125in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 150 °C Temperature 302 °F 　
　 4.4 4.4 0.8mm (0.031in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 120 °C Temperature 248 °F 　
　 4.4 4.4 1.6mm (0.062in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 120 °C Temperature 248 °F 　
　 4.4 4.4 3.2mm (0.125in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 120 °C Temperature 248 °F 　
　 4.4 4.4 3.2mm (0.125in); ASTM D 150
　 @Frequency 1000 Hz, @Frequency 1000 Hz, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 4.4 4.4 0.8mm (0.031in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 4.4 4.4 0.8mm (0.031in); ASTM D 150
　 @Frequency 1.00e+6 Hz, @Frequency 1.00e+6 Hz, 　
　 Temperature 200 °C Temperature 392 °F 　
　 4.4 4.4 0.8mm (0.031in); ASTM D 150
　 @Frequency 1.00e+6 Hz, @Frequency 1.00e+6 Hz, 　
　 Temperature 150 °C Temperature 302 °F 　
　 4.5 4.5 3.2mm (0.125in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 200 °C Temperature 392 °F 　
　 4.5 4.5 1.6mm (0.062in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 200 °C Temperature 392 °F 　
　 4.5 4.5 0.8mm (0.031in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 200 °C Temperature 392 °F 　
　 4.5 4.5 0.8mm (0.031in); ASTM D 150
　 @Frequency 1000 Hz, @Frequency 1000 Hz, 　
　 Temperature 200 °C Temperature 392 °F 　
　 4.5 4.5 0.8mm (0.031in); ASTM D 150
　 @Frequency 1000 Hz, @Frequency 1000 Hz, 　
　 Temperature 120 °C Temperature 248 °F 　
　 4.5 4.5 0.8mm (0.031in); ASTM D 150
　 @Frequency 1000 Hz, @Frequency 1000 Hz, 　
　 Temperature 150 °C Temperature 302 °F 　
　 4.8 4.8 3.2mm (0.125in); ASTM D 150
　 @Frequency 1.00e+6 Hz, @Frequency 1.00e+6 Hz, 　
　 Temperature 150 °C Temperature 302 °F 　
　 4.8 4.8 3.2mm (0.125in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 250 °C Temperature 482 °F 　
　 4.8 4.8 3.2mm (0.125in); ASTM D 150
　 @Frequency 1.00e+6 Hz, @Frequency 1.00e+6 Hz, 　
　 Temperature 120 °C Temperature 248 °F 　
　 4.8 4.8 3.2mm (0.125in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 250 °C Temperature 482 °F 　
　 4.8 4.8 3.2mm (0.125in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 250 °C Temperature 482 °F 　
　 4.9 4.9 3.2mm (0.125in); ASTM D 150
　 @Frequency 1.00e+6 Hz, @Frequency 1.00e+6 Hz, 　
　 Temperature 200 °C Temperature 392 °F 　
　 5 5 3.2mm (0.125in); ASTM D 150
　 @Frequency 1000 Hz, @Frequency 1000 Hz, 　
　 Temperature 200 °C Temperature 392 °F 　
　 5 5 3.2mm (0.125in); ASTM D 150
　 @Frequency 1000 Hz, @Frequency 1000 Hz, 　
　 Temperature 150 °C Temperature 302 °F 　
　 5 5 3.2mm (0.125in); ASTM D 150
　 @Frequency 1000 Hz, @Frequency 1000 Hz, 　
　 Temperature 120 °C Temperature 248 °F 　
Dielectric Strength   27.0 kV/mm 686 kV/in Short time; ASTM D149
　 @Thickness 3.20 mm, @Thickness 0.126 in, 　
　 Temperature 150 °C Temperature 302 °F 　
　 28.0 kV/mm 711 kV/in Short time; ASTM D149
　 @Thickness 3.20 mm, @Thickness 0.126 in, 　
　 Temperature 120 °C Temperature 248 °F 　
　 29.0 kV/mm 737 kV/in Short time; ASTM D149
　 @Thickness 3.20 mm, @Thickness 0.126 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 31.0 kV/mm 787 kV/in Short time; ASTM D149
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 150 °C Temperature 302 °F 　
　 33.0 kV/mm 838 kV/in Short time; ASTM D149
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 120 °C Temperature 248 °F 　
　 33.0 kV/mm 838 kV/in Short time; ASTM D149
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 200 °C Temperature 392 °F 　
　 35.0 kV/mm 889 kV/in Short time; ASTM D149
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 37.0 kV/mm 940 kV/in Short time; ASTM D149
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 150 °C Temperature 302 °F 　
　 40.0 kV/mm 1020 kV/in Short time; ASTM D149
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 200 °C Temperature 392 °F 　
　 40.0 kV/mm 1020 kV/in Short time; ASTM D149
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 41.0 kV/mm 1040 kV/in Short time; ASTM D149
　 @Thickness 0.800 mm, @Thickness 0.0315 in, 　
　 Temperature 120 °C Temperature 248 °F 　
Dissipation Factor   0.004 0.004 0.8mm (0.031in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 0.004 0.004 1.6mm (0.062in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 0.004 0.004 3.2mm (0.125in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 0.006 0.006 3.2mm (0.125in); ASTM D 150
　 @Frequency 1000 Hz, @Frequency 1000 Hz, 　
　 Temperature 120 °C Temperature 248 °F 　
　 0.007 0.007 3.2mm (0.125in); ASTM D 150
　 @Frequency 1000 Hz, @Frequency 1000 Hz, 　
　 Temperature 150 °C Temperature 302 °F 　
　 0.008 0.008 0.8mm (0.031in); ASTM D 150
　 @Frequency 1000 Hz, @Frequency 1000 Hz, 　
　 Temperature 120 °C Temperature 248 °F 　
　 0.009 0.009 0.8mm (0.031in); ASTM D 150
　 @Frequency 1000 Hz, @Frequency 1000 Hz, 　
　 Temperature 150 °C Temperature 302 °F 　
　 0.009 0.009 3.2mm (0.125in); ASTM D 150
　 @Frequency 1.00e+6 Hz, @Frequency 1.00e+6 Hz, 　
　 Temperature 200 °C Temperature 392 °F 　
　 0.01 0.01 0.8mm (0.031in); ASTM D 150
　 @Frequency 1.00e+6 Hz, @Frequency 1.00e+6 Hz, 　
　 Temperature 200 °C Temperature 392 °F 　
　 0.012 0.012 0.8mm (0.031in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 120 °C Temperature 248 °F 　
　 0.013 0.013 3.2mm (0.125in); ASTM D 150
　 @Frequency 1000 Hz, @Frequency 1000 Hz, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 0.013 0.013 0.8mm (0.031in); ASTM D 150
　 @Frequency 1000 Hz, @Frequency 1000 Hz, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 0.014 0.014 3.2mm (0.125in); ASTM D 150
　 @Frequency 1000 Hz, @Frequency 1000 Hz, 　
　 Temperature 200 °C Temperature 392 °F 　
　 0.014 0.014 1.6mm (0.062in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 120 °C Temperature 248 °F 　
　 0.015 0.015 0.8mm (0.031in); ASTM D 150
　 @Frequency 1000 Hz, @Frequency 1000 Hz, 　
　 Temperature 200 °C Temperature 392 °F 　
　 0.016 0.016 0.8mm (0.031in); ASTM D 150
　 @Frequency 1.00e+6 Hz, @Frequency 1.00e+6 Hz, 　
　 Temperature 150 °C Temperature 302 °F 　
　 0.016 0.016 3.2mm (0.125in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 120 °C Temperature 248 °F 　
　 0.018 0.018 0.8mm (0.031in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 150 °C Temperature 302 °F 　
　 0.018 0.018 3.2mm (0.125in); ASTM D 150
　 @Frequency 1.00e+6 Hz, @Frequency 1.00e+6 Hz, 　
　 Temperature 150 °C Temperature 302 °F 　
　 0.02 0.02 1.6mm (0.062in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 150 °C Temperature 302 °F 　
　 0.023 0.023 3.2mm (0.125in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 150 °C Temperature 302 °F 　
　 0.025 0.025 0.8mm (0.031in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 200 °C Temperature 392 °F 　
　 0.026 0.026 0.8mm (0.031in); ASTM D 150
　 @Frequency 1.00e+6 Hz, @Frequency 1.00e+6 Hz, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 0.027 0.027 3.2mm (0.125in); ASTM D 150
　 @Frequency 1.00e+6 Hz, @Frequency 1.00e+6 Hz, 　
　 Temperature 23.0 °C Temperature 73.4 °F 　
　 0.028 0.028 1.6mm (0.062in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 200 °C Temperature 392 °F 　
　 0.032 0.032 3.2mm (0.125in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 200 °C Temperature 392 °F 　
　 0.032 0.032 3.2mm (0.125in); ASTM D 150
　 @Frequency 1.00e+6 Hz, @Frequency 1.00e+6 Hz, 　
　 Temperature 120 °C Temperature 248 °F 　
　 0.034 0.034 3.2mm (0.125in); ASTM D 2520 B
　 @Frequency 1.00e+9 Hz, @Frequency 1.00e+9 Hz, 　
　 Temperature 250 °C Temperature 482 °F 　
Comparative Tracking Index  100 - 174 V 100 - 174 V UL 746A
　 　 　 　
Thermal Properties Metric English Comments
CTE, linear   -5.00 µm/m-°C -2.78 µin/in-°F ISO 11359-1/-2
　 @Thickness 2.00 mm, @Thickness 0.0787 in, 　
　 Temperature 160 - 260 °C Temperature 320 - 500 °F 　
　 -2.00 µm/m-°C -1.11 µin/in-°F ISO 11359-1/-2
　 @Thickness 4.00 mm, @Thickness 0.157 in, 　
　 Temperature 160 - 260 °C Temperature 320 - 500 °F 　
　 1.00 µm/m-°C 0.556 µin/in-°F ISO 11359-1/-2
　 @Thickness 2.00 mm, @Thickness 0.0787 in, 　
　 Temperature -40.0 - 260 °C Temperature -40.0 - 500 °F 　
　 2.00 µm/m-°C 1.11 µin/in-°F ISO 11359-1/-2
　 @Thickness 4.00 mm, @Thickness 0.157 in, 　
　 Temperature -40.0 - 260 °C Temperature -40.0 - 500 °F 　
　 2.00 µm/m-°C 1.11 µin/in-°F ISO 11359-1/-2
　 @Thickness 2.00 mm, @Thickness 0.0787 in, 　
　 Temperature -40.0 - 23.0 °C Temperature -40.0 - 73.4 °F 　
　 2.00 µm/m-°C 1.11 µin/in-°F ISO 11359-1/-2
　 @Thickness 2.00 mm, @Thickness 0.0787 in, 　
　 Temperature 55.0 - 160 °C Temperature 131 - 320 °F 　
　 3.00 µm/m-°C 1.67 µin/in-°F ISO 11359-1/-2
　 @Thickness 4.00 mm, @Thickness 0.157 in, 　
　 Temperature 55.0 - 160 °C Temperature 131 - 320 °F 　
　 3.00 µm/m-°C 1.67 µin/in-°F ISO 11359-1/-2
　 @Thickness 4.00 mm, @Thickness 0.157 in, 　
　 Temperature -40.0 - 23.0 °C Temperature -40.0 - 73.4 °F 　
　 3.00 µm/m-°C 1.67 µin/in-°F ISO 11359-1/-2
　 @Thickness 4.00 mm, @Thickness 0.157 in, 　
　 Temperature 23.0 - 55.0 °C Temperature 73.4 - 131 °F 　
　 3.00 µm/m-°C 1.67 µin/in-°F ISO 11359-1/-2
　 @Thickness 2.00 mm, @Thickness 0.0787 in, 　
　 Temperature 23.0 - 55.0 °C Temperature 73.4 - 131 °F 　
　 5.00 µm/m-°C 2.78 µin/in-°F ASTM E 228
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 23.0 - 150 °C Temperature 73.4 - 302 °F 　
　 13.0 µm/m-°C 7.22 µin/in-°F ASTM E 228
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 23.0 - 150 °C Temperature 73.4 - 302 °F 　
CTE, linear, Transverse to Flow   60.0 µm/m-°C 33.3 µin/in-°F ISO 11359-1/-2; 2mm
　 @Temperature -40.0 - 23.0 °C @Temperature -40.0 - 73.4 °F 　
　 61.0 µm/m-°C 33.9 µin/in-°F ISO 11359-1/-2; 4mm
　 @Temperature -40.0 - 23.0 °C @Temperature -40.0 - 73.4 °F 　
　 85.0 µm/m-°C 47.2 µin/in-°F ISO 11359-1/-2; 2mm
　 @Temperature -40.0 - 260 °C @Temperature -40.0 - 500 °F 　
　 88.0 µm/m-°C 48.9 µin/in-°F ISO 11359-1/-2; 4mm
　 @Temperature -40.0 - 260 °C @Temperature -40.0 - 500 °F 　
　 37.0 µm/m-°C 20.6 µin/in-°F ASTM E 228
　 @Thickness 3.17 mm, @Thickness 0.125 in, 　
　 Temperature 23.0 - 150 °C Temperature 73.4 - 302 °F 　
　 49.0 µm/m-°C 27.2 µin/in-°F ASTM E 228
　 @Thickness 1.60 mm, @Thickness 0.0630 in, 　
　 Temperature 23.0 - 150 °C Temperature 73.4 - 302 °F 　
　 68.0 µm/m-°C 37.8 µin/in-°F ISO 11359-1/-2
　 @Thickness 2.00 mm, @Thickness 0.0787 in, 　
　 Temperature 23.0 - 55.0 °C Temperature 73.4 - 131 °F 　
　 70.0 µm/m-°C 38.9 µin/in-°F ISO 11359-1/-2
　 @Thickness 4.00 mm, @Thickness 0.157 in, 　
　 Temperature 23.0 - 55.0 °C Temperature 73.4 - 131 °F 　
　 88.0 µm/m-°C 48.9 µin/in-°F ISO 11359-1/-2
　 @Thickness 2.00 mm, @Thickness 0.0787 in, 　
　 Temperature 55.0 - 160 °C Temperature 131 - 320 °F 　
　 92.0 µm/m-°C 51.1 µin/in-°F ISO 11359-1/-2
　 @Thickness 4.00 mm, @Thickness 0.157 in, 　
　 Temperature 55.0 - 160 °C Temperature 131 - 320 °F 　
　 101 µm/m-°C 56.1 µin/in-°F ISO 11359-1/-2
　 @Thickness 2.00 mm, @Thickness 0.0787 in, 　
　 Temperature 160 - 260 °C Temperature 320 - 500 °F 　
　 107 µm/m-°C 59.4 µin/in-°F ISO 11359-1/-2
　 @Thickness 4.00 mm, @Thickness 0.157 in, 　
　 Temperature 160 - 260 °C Temperature 320 - 500 °F 　
Melting Point  335 °C 635 °F ASTM D 3418
　 335 °C 635 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  275 °C 527 °F ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi)  265 °C 509 °F ASTM D 648
　 268 °C 514 °F ISO 75-1/-2
Glass Transition Temp, Tg  120 °C 248 °F ASTM D 3418
UL RTI, Electrical   240 °C 464 °F UL 746B
　 @Thickness 0.750 mm @Thickness 0.0295 in 　
　 240 °C 464 °F UL 746B
　 @Thickness 1.50 mm @Thickness 0.0591 in 　
　 240 °C 464 °F UL 746B
　 @Thickness 3.00 mm @Thickness 0.118 in 　
UL RTI, Mechanical with Impact   220 °C 428 °F UL 746B
　 @Thickness 0.750 mm @Thickness 0.0295 in 　
　 220 °C 428 °F UL 746B
　 @Thickness 1.50 mm @Thickness 0.0591 in 　
　 220 °C 428 °F UL 746B
　 @Thickness 3.00 mm @Thickness 0.118 in 　
UL RTI, Mechanical without Impact   240 °C 464 °F UL 746B
　 @Thickness 1.50 mm @Thickness 0.0591 in 　
　 240 °C 464 °F UL 746B
　 @Thickness 0.750 mm @Thickness 0.0295 in 　
　 240 °C 464 °F UL 746B
　 @Thickness 3.00 mm @Thickness 0.118 in 　
Flammability, UL94   V-0 V-0 IEC 60695-11-10
　 @Thickness 1.50 mm @Thickness 0.0591 in 　
　 V-0 V-0 IEC 60695-11-10
　 @Thickness 0.380 mm @Thickness 0.0150 in 　
　 V-0 V-0 IEC 60695-11-10
　 @Thickness 0.750 mm @Thickness 0.0295 in 　
　 V-0 V-0 UL94
　 @Thickness 0.380 mm @Thickness 0.0150 in 　
　 V-0 V-0 UL94
　 @Thickness 0.750 mm @Thickness 0.0295 in 　
　 V-0 V-0 UL94
　 @Thickness 1.50 mm @Thickness 0.0591 in 　
　 V-0 V-0 IEC 60695-11-10
　 @Thickness 3.00 mm @Thickness 0.118 in 　
　 V-0 V-0 UL94
　 @Thickness 3.00 mm @Thickness 0.118 in 　
Oxygen Index  0.38 0.38 ASTM D2863
　 @Thickness 3.17 mm @Thickness 0.125 in 　
　 　 　 　
Processing Properties Metric English Comments
Melt Temperature  355 °C 671 °F Optimum
　 350 - 360 °C 662 - 680 °F 　
Mold Temperature  80.0 °C 176 °F Optimum
　 40.0 - 150 °C 104 - 302 °F 　
Drying Temperature  150 °C 302 °F 　
Dry Time  3 hour 3 hour Dehumidified Dryer
Moisture Content  <= 0.010 % <= 0.010 % 　
　 　 　 　
Descriptive Properties 　 　 　
Color Cream 　 　
Drying Recommended Yes 　 　
Features Appearance, Pleasing Surface 　 　
　 Arc Resistant 　 　
　 Aromatic 　 　
　 Chemical Resistance, Good 　 　
　 Dimensional Stability, Good 　 　
　 Flow, Good 　 　
　 Heat Aging Resistance, Good 　 　
　 Moisture Absorption, Low 　 　
　 Platable 　 　
　 Platable 　 　
Filler Glass fiber reinforcement 　 　
Flame Retardant - Halogen/Red Phosphorus Free Yes 　 　
Forms Pellets 　 　
Generic LCP 　 　
Part Marking Code >LCP-GF30< 　 ISO 11469
Polymer Family LCP 　 　
Polymer Type LCP 　 　
Processing Injection Moldable 　 　
Processing Method Injection Molding 　 　
Product Category Electrical Resins 　 　
　 Flame Retardant Resins 　 　
　 Glass Reinforced Resins 　 　
Region Available Americas 　 　
　 Asia/Pacific 　 　
　 Europe 　 　
Resin Identification LCP-GF30 　 ISO 1043
Uses Automotive Applications 　 　
　 Automotive Electronics 　 　
　 Automotive, Under the Hood 　 　
　 Communication Applications 　 　
　 Computer Components 　 　
　 Connectors 　 　
　 Electrical/Electronic Applications 　 　
　 Parts, Engineering 　 　
　 Parts, Thin-walled 　 　
　 Printer Parts 　 　

产品特性：

★高温电气/ 电子装配：能承受SMT 装配工序操作，包括无铅回流焊接。
★卓越的热老化性能，在高温下保持固有特性。
★卓越的流动性- 薄壁，复杂的形状。
★尺寸稳定性极佳，模塑收缩率低，热膨胀系数极小，可与金属相媲美。
★在成型时，分子链朝着流动的方向排列，产生一种好似其分子自身将其增强的自增强效果可获得极高的强度和弹性模量。
★优异的耐化学腐蚀性。
★模塑速度：周期循环极快。
★卓越的抗蠕变性。
★阻燃性。
★在宽广的温度范围内具有卓越的介电性能。
 

 

 

 


价格：25.00元/KG
立即购买
点击这里给我发消息 点击这里给我发消息